5.08mm ptich tin-plated brass material terminals Brass Contact wire crimp terminals

Product Details:

Place of Origin:	Dongguan, China(mainland)
Brand Name:	HRT
Certification:	ISO9001/ ISO14001/UL/RoHS/REACH
Model Number:	C5080M-T

Payment & Shipping Terms:

Minimum Order Quantity:	75K PCS
Price:	Negotiated
Packaging Details:	paper tray with out carton
Delivery Time:	5 to 8 working days after payment checked
Payment Terms:	TT, Western Union, PayPal, L/C
Supply Ability:	100 million pcs per month

Contact Now

Detailed Product Description

Pitch:	5.08mm	Wire Range:	AWG#18- #24
Material:	Brass	Finish:	Tin-plated
Terminal Type:	Crimp Terminal	Insulation O.D:	2.50mm(Max)
High Light:	Crimp Terminal Connector , Connector Crimp Terminal

1, The specification of the product including basic size information, electrical and mechanical properties.

Basic size information
Termination Interface Style		Crimp or compression
Processing methods		E-stamping before tin-plated
Insulation O.D.		2.50mm(Max)
Part No.		C5080M-T-A or C5080M-T-B
Application		Signal
Package		7K/reel

Electrical properties
Current Rating		10A AC, DC
Voltage Rating		250V AC, DC
Contact Resistance		10mΩ Max
Insulation Resistance		1000mΩ min
Withstanding Voltage		1500V AC/minute

Mechanical properties
Temperature range		-25℃ to 85 ℃
Other information please kindly check the following picture.

2, Related drawing and report

5.08mm ptich tin-plated brass material terminals Brass Contact wire crimp terminals

The following pictures are engineering drawing and testing report for your reference, wish these can help you to purchase the ideal and right parts from us. Thank you!

5. Mechanical Performance

Test Description		Procedure	Requirement
5-1	Actuator Insertion & Withdrawal Force	Insert and withdraw connectors at the speed rate of 25±3mm / minute.	Refer to paragraph 7
5-2	Crimping Pull Out Force	Fix the crimped terminal, apply axial pull out force on the wire at the speed rat of 25±3mm / minute.(Based upon JIS C5402 6.8)	AWG#14	11.0kgf (Min)
			AWG#16	10.0kgf (Min)
			AWG#18	9.0kgf (Min)
			AWG#20	6.0kgf (Min)
			AWG#22	4.0kgf (Min)
			AWG#24	3.0kgf (Min)
5-3	Terminal Insertion Force.	Insert the crimped terminal into the housing.	2.00kgf (Max.)
5-4	Terminal/Housing Retention Force.	Apply axial pull out force at the speed rate of 25±3mm / minute on the terminal assembled in the housing.	3.00kgf (Min.)
5-5	Pin Retention Force	Apply axial push force at the speed rate of 25±3mm / minute	2.0kgf (Min.)
5-6	Durability	When mated up to 50 cycles repeatedly by the rate of 10 cycle per minute.	Contact Resistance 20mΩ (Max.)
5-7	Vibration	Amplitude: 1.5mm P-P Sweep time: 10-55-10 Hz in 1 minute Duration: 2 hours in each X.Y.Z. axes. (Based upon MIL-STD-202 Method 201A)	Appearance No Damage. Contact Resistance 20mΩ (Max.) Discontinuity 1 μsec.(Max.)
5-8	Physical Shock	490m/s²｛50G｝,3 strokes in each X.Y.Z. axes. (Based upon JIS C0041/MIL-STD-202 Method 213B Cond. A)

6. Environmental Performance And Others

Test Description		Procedure	Requirement
6-1	Temperature Rise	Carrying rated current load.(Based upon UL 498)	30℃(Max.)
6-2	Heat Resistance	85±2℃,96 hours (Based upon JIS C0021/MIL-STD-202 Method 108A Cond. A)	Appearance No Damage. Contact Resistance 20mΩ (Max.)
6-3	Cold Resistance	-25±3℃,96 hours (Based upon JIS C0020)	Appearance No Damage. Contact Resistance 20mΩ (Max.)
6-4	Humidity	Temperature: 40±2℃ Relative Humidity : 90~95% Duration: 96 hours (Based upon JIS C0022/MIL-STD-202 Method 103B Cond. B)	Appearance No Damage. Contact Resistance 20mΩ (Max.) Insulation Resistance 100MΩ (Min.) Dielectric Withstanding Voltage Must meet 4-3
6-5	Temperature Cycling	5 cycles of: a) -55℃ 30 minutes b) +85℃ 30 minutes (Based upon JIS C0025)	Appearance No Damage. Contact Resistance 20mΩ (Max.)
6-6	Salt Spray	Tin-plated 12 hours / Gold- plated 24 hours exposure to a salt spray from the 5±1% solution at 35±2℃. (Based upon JIS C0023/MIL-STD-202 Method 101D Cond. B)
6-7	SO2 Gas	24 hours exposure to 50±5ppm. SO2 gas at 40±2℃.
6-8	NH3 Gas	40 minutes exposure to NH3 gas evaporating from 28% Ammonia solution.